Nanomechanical characterization of recalcitrant foulants and hollow fiber membranes in ultrafiltration systems
Résumé
Long-term nanomechanical changes of polymeric ultrafiltration (UF) membranes caused by
fouling/cleaning agents in water treatment are not well established in the literature. The goal of this
study was to investigate the nanomechanical properties of polymeric UF hollow fiber membranes
operating at a pilot-scale for 449 d and subjected to a low-quality feed (i.e., high turbidity/TOC
content). Quantitative nanomechanical mapping technique was used to measure the deformation,
dissipation, modulus, adhesion, and roughness of the polymeric structures of commercial Aquaflex
virgin membranes, harvested membranes, and foulant layers. Results indicated that the recalcitrant
and heterogeneous nature of the foulants absorbed on harvested membranes showed low elastic
properties, and high modulus, adhesion, and roughness. The strong affinity of these foulants towards
membrane surface would alter membrane characteristics and influence subsequent fouling behaviour.
The cleaning process and extended operation did not significantly affect the nanomechanical proper-
ties of membranes. Despite the low-quality feed, the three modules were only subjected to 37 chemi-
cal-enhanced backwashes and filtered a total volume of 2.155 m3. These results indicate the importance
of operating conditions (i.e., frequency of backwash/cleaning/disinfection steps) and feed quality on
the long-term changes of UF membranes and would assist in identifying research directions that are
necessary to minimize membrane fouling/ageing.